ORAFOL ORACAL 970RA-990 Aubergine Bronze Matte Premium Wrapping Shift Effect Cast Vinyl RapidAir
ORACAL® 970RA Premium Shift Effect Cast with RapidAir® Technology
4.25-mil, multi-layered, high performance cast PVC wrapping film engineered with cutting edge technology that produces
mesmerizing multi-color effects. This unique shade shifting occurs as a result of your viewing angle and incidence of light. Shift
your view and the color change begins. Available in 19 colors including gloss and matte finishes.
88# PE-coated silicone paper featuring advanced air release technology to facilitate quicker, easier application
Grey, solvent polyacrylate, repositionable, permanent adhesive that with heat can be removed with little or no adhesive residue
for up to four years
Area of Use
Specially developed for short- to medium-term, complete wraps of fleet and motor sport vehicles in solid, opaque colors.
Conforms over curved surfaces, rivets and corrugations. Does not require overlaminate.
Thickness* (without liner and adhesive) 4.25-mil
Dimensional Stability (FINAT TM-14) Adhered to steel, shrinkage <.004 Temperature Resistance** Adhered to aluminum, -58°F to +248°F, no variation Fire Behavior (DIN 75200) Fire Rating Adhered to steel, self-extinguishing ASTM E 84-07 Class A Adhesive Power* (FINAT TM-1, after 24 h) Adhered to stainless steel: 3.65 lb/in Tensile Strength (DIN EN ISO 527) Along: Min. 21 MPa Across: Min. 21 MPa Elongation at Break (DIN EN ISO 527) Along: Min. 120% Across: Min. 120% Seawaterability (DIN 50021) Adhered to aluminum, after 100h/95°F, no variation Shelf Life*** 2 years Minimum Life Expectancy**** (bracketed durability used for applications onto all types of watercrafts) 4 (2) years Minimum Application Temperature 59°F Available Lengths Available Widths 150 (50-yard), 75 (25-yard), 30 (10-yard) 60
*average **short-term exposure *** in original packaging, at 68°F and 50% relative humidity **** standard central European climate
vertical outdoor exposure
Surfaces to which the material will be applied must be thoroughly cleaned from dust, grease or any contamination which could affect the
adhesion of the material. Freshly lacquered or painted surfaces should be completely cured. The compatibility of selected lacquers and paints
should be tested by the user, prior to application of the material. Films with structured surface are naturally more sensitive than the
unstructured. Accordingly, these films are to be treated carefully both in processing and in cleaning. Impurities affect the appearance of
structured films and require more frequent cleaning. Furthermore the application information published by ORAFOL is to be considered. The
batch traceability according to ISO 9001 is possible on the basis of the roll number.