• Reduced gloss finish prevents reflection
• Designed for use in window and mirror graphics
• More sparkle and shimmer than Oracal Etched Glass Vinyl
• 3 mil cast vinyl with synthetic liner
• Permanent solvent adhesive
• 7 year durability
Cast PVC film for high quality glass decoration with very good weather resistance an UV stability. The
reduced gloss and the roughly structured surface inhibits undesired reflection.
Special polyester film, 100 micron
Solvent polyacrylate, permanent
Area of use
Developed for glass areas, to achieve a hoar-frost or freezing effect; especially for the decorative designing
of shop windows and glass doors.
Suitable for manufacturing on cutting systems.
Wet application is recommended.
Thickness* 80 micron
Dimensional stability adhered to glass shrinkage 0.1 mm max.
Temperature resistance adhered to glass, -40°C to +90°C, no variation
(FINAT TM 1, after 24h) 16 N/25 mm
16 N/25 mm
Tensile strength (DIN EN ISO 527)
along 9 MPa min.
across 9 MPa min.
Elongation at break (DIN EN ISO 527)
along 40% min.
across 40% min.
Shelf life** 2 years
Application temperature > + 8°C
Service life by specialist application
under vertical outdoor exposure
(normal climate of Central Europe)
Surfaces to which the material will be applied must be thoroughly cleaned from dust, grease or any
contamination which could affect the adhesion of the material. Furthermore the application information
published by ORAFOL is to be considered. The batch traceability according to ISO 9001 is possible on
the basis of the roll number.
(FINAT TM 14)
(without protective paper and adhesive)
** in original packaging, at 20°C and 50% relative humidity
Resistance to cleaning agents adhered to glass, 8h in washalcalics (0,5% householdcleaning
agents) in room temperature and in 65°C, no variation
Fire behaviour Only flame resistant (class DIN 4102-B1) on glass with a
moulded density of >= 2250 kg/m³ (indoor application)
The statements in this information sheet are based upon our knowledge and practical experience. This data is intended only as a source of
information and is given without guarantee and does not constitute a warranty. Due to the wide variety of possible uses and applications customers
should independently determine the suitability of this material for their specific purpose, prior to use.